Superaustenitic X1CrNiMoCuN20-18-7

1.4547 · X1CrNiMoCuN20-18-7 · 254SMO

Indicative reference data. Always check the supplier's mill certificate (3.1) before using them on critical parts.

EN 1.4547Designación X1CrNiMoCuN20-18-7DIN X1CrNiMoCuN20-18-7AISI/SAE 254SMOUNS S31254JIS SUS312L (aprox.)ASTM A240 S31254 / A276 / A182 F44AFNOR Z1CNDU20-18-06BS S31254GB/T 015Cr20Ni18Mo6CuN / 022Cr20Ni18Mo6CuNISO 15510 X1CrNiMoCuN20-18-7Alias F44Alias AL-6XN (approx.)Alias Sanicro 28 (aprox.)Alias super austenitic stainlessAlias 6% Mo stainless
See recommended Vc and feed →

Indicative chemical composition (%)

C ≤0.020Si ≤0.80Mn ≤1.00P ≤0.030S ≤0.010Cr 19.5-20.5Ni 17.5-18.5Mo 6.00-6.50Cu 0.50-1.00N 0.18-0.22

Mechanical properties

Densidad

8 g/cm³

Resistencia a tracción (Rm)

650-850 MPa

Límite elástico (Re)

≥300 MPa

Alargamiento (A%)

≥35 %

Thermal properties

Conductividad térmica

13 W/m·K

Dilatación térmica

16.5 µm/m·K

Electrical and machinability

Resistividad eléctrica

0.73 µΩ·m

Maquinabilidad

Difícil (índice 25)

Soldabilidad: Good

Corrosion resistance: Outstanding against chloride pitting and cracking, better than 904L

Heat treatable: No

Workshop behavior

Magnetic: No (Puede volverse ligeramente magnético tras deformación en frío intensa.)

Refrigerante recomendado: Emulsión soluble de alta concentración (8-12%) o aceite entero; refrigeración abundante para evitar el frotamiento.

Control de viruta: Viruta larga y tenaz, tiende a enredarse; usa geometría rompevirutas agresiva.

Rugosidad Ra alcanzable: 0.8-3.2 (el filo de aportación limita el acabado muy fino a Vc bajas) µm

Resistencia a fatiga: Buena; el pulido superficial eleva notablemente el límite de fatiga.

Impact resistance: Excelente, incluso a temperaturas criogénicas.

Typical uses

  • Intercambiadores de agua de mar
  • plantas desaladoras
  • industria de celulosa

Machining notes and operator tips

Of the most corrosion-resistant austenitic stainless steels; very tenacious, treat as difficult material.

Vc · Torno (metal duro, corte medio): 67-111 m/min

Vc · Fresado (metal duro, corte medio): 39-67 m/min

  • Mantén siempre un avance mínimo; el frotamiento (Vc alta con avance bajo) es la causa nº1 de endurecimiento superficial.
  • Usa geometría de filo positiva y aristas muy afiladas; cambia la plaquita antes de que el desgaste de flanco sea visible.
  • No pares el avance a mitad de pasada: la pieza se endurece localmente y complica el pase siguiente.

Adjust Vc per tool, cut type and shop pace in the Vc/feed calculator ↑.

Calculate weight and cost of raw bar

Peso estimado

2.513 kg

Materials in the same family

X5CrNi18-10 Austenitic stainless X5CrNi18-10X2CrNi19-11 Low Carbon Austenitic Stainless X2CrNi19-11X5CrNiMo17-12-2 Austenitic stainless X5CrNiMo17-12-2X2CrNiMo17-12-2 Low Carbon Austenitic Stainless X2CrNiMo17-12-2X6CrNiTi18-10 Stabilized austenitic stainless X6CrNiTi18-10X8CrNiS18-9 Easy-machining austenitic stainless X8CrNiS18-9X1NiCrMoCu25-20-5 Superaustenitic X1NiCrMoCu25-20-5X6CrNiMoTi17-12-2 Stabilized austenitic stainless X6CrNiMoTi17-12-2X2CrNiMo18-15-4 Austenitic stainless X2CrNiMo18-15-4X15CrNiSi20-12 Inoxidable refractario X15CrNiSi20-12X15CrNiSi25-21 Inoxidable refractario X15CrNiSi25-21X12CrMnNiN17-7-5 Economical Austenitic Stainless X12CrMnNiN17-7-5
See the full material catalogue

Related tools

Hardness converter

Convierte durezas de taller: HRC, HRB, HRA, HRD, superficiales N/T, Brinell, Vickers, Knoop, Shore HS y Rm, con tabla propia por familia de material. Calcula también la dureza desde la huella y avisa de cuándo el ensayo no vale.

Cutting parameters calculator